P01 - High Bright and Sheen Kaolin
Introduction:
High Bright and Lustrous Kaolin - P01 has features of high brightness, high luster, low yellowness, low viscosity and minor particle size. It is suitable to be used as dope for top coat of high class coating paper.
When the quantity of the dispersant Polypropylene is 0.01~0.12% in producing, P01 may occur as dispersoid with 70-71% solid content and excellent fluid.
The main parameters of the product:
|
GE Brightness(YQ-Z-48B)
|
%
|
86.0±1.0
|
|
Particle Size (-2µ)(Sedigraph5000)
|
%
|
90.0～94.0
|
|
Viscosity(NDJ-1.60rpm500mpa.s)
|
%
|
65.0～68.0
|
|
Moisture Content
|
%
|
≤1.5
|
|
Residue in 325 mesh
|
%
|
≤0.01
|
|
PH
|
|
5~7
|
|
Loss after ignition
|
%
|
13.0~14.0
|
|
SiO2
|
％
|
≤47.0
|
|
Al2O3
|
%
|
≥37.0
|
|
Fe2O3
|
%
|
≤0.6
|
P02 - High Bright Kaolin
Introduction:
High Bright Kaolin - P02 has features of high brightness and minor particle size. It is suitable to be used as dope for top coat of high class coating paper when it is coated at medium or low speed.
When the quantity of the dispersant Polypropylene is 0.12% in producing, P02 may occur as dispersoid with 65-68% solid content and excellent fluid.
The main parameters of the product:
|
GE Brightness(YQ-Z-48B)
|
%
|
≥85.0
|
|
Particle Size (-2µ)(Sedigraph5000)
|
%
|
≥85.0
|
|
Viscosity(NDJ-1.60rpm500mpa.s)
|
%
|
≥66.0
|
|
Moisture Content
|
%
|
≤1.5
|
|
Residue in 325 mesh
|
%
|
≤0.01
|
|
PH
|
|
5~7
|
|
Loss after ignition
|
%
|
13.0~14.0
|
|
SiO2
|
％
|
≤47.0
|
|
Al2O3
|
%
|
≥37.0
|
|
Fe2O3
|
%
|
≤0.6
|
PP01 - Superfine Kaolin
Introduction:
Superfine Kaolin - PP01, the newly production is especially suitable for the use as dope for the high quality paper and cardboard. It can greatly increase the printing lustrous degree of the paper and cardboard and make them much easier to be decorated.
When the quantity of the dispersant Polypropylene is 0.01~0.12% in producing, PP01 may occur as dispersoid with 70-71% solid content and excellent fluid.
The main parameters of the product:
|
GE Brightness(YQ-Z-48B)
|
%
|
≥86.5
|
|
Particle Size (-2µ)(Sedigraph5000)
|
%
|
≥96
|
|
Viscosity(NDJ-1.60rpm500mpa.s)
|
%
|
≥68.5
|
|
Moisture Content
|
%
|
≤1.5
|
|
Residue in 325 mesh
|
%
|
≤0.01
|
|
PH
|
|
5~7
|
|
Loss after ignition
|
%
|
13.0~14.0
|
|
SiO2
|
％
|
≤47.0
|
|
Al2O3
|
%
|
≥37.0
|
|
Fe2O3
|
%
|
≤0.6
|
P04 -Painting Kaolin
Introduction:
P04 has features of good crystallization and decentrality, high purity, minor particle, and moderate degree of oil absorption. It is suited to be used to produce dope for top grade paint.
The main parameters of the product:
|
GE Brightness(YQ-Z-48B)
|
%
|
≥83.0
|
|
Particle Size (-2µ)(Sedigraph5000)
|
%
|
74.0-78.0
|
|
Viscosity(NDJ-1.60rpm500mpa.s)
|
%
|
40.0~55.0
|
|
Moisture Content
|
%
|
≤1.5
|
|
Residue in 325 mesh
|
%
|
≤0.01
|
|
PH
|
|
5~7
|
|
Loss after ignition
|
%
|
13.0~14.0
|
|
SiO2
|
％
|
≤48.0
|
|
Al2O3
|
%
|
≥36.0
|
|
Fe2O3
|
%
|
≤0.65
|
P08 - Ceramic Kaolin
Introduction: P08 is made for special ceramic.
The main parameters of the product:
|
GE Brightness(YQ-Z-48B)
|
%
|
84.0±1.0
|
|
Particle Size (-2µ)(Sedigraph5000)
|
%
|
≥85.0
|
|
Viscosity(NDJ-1.60rpm500mpa.s)
|
%
|
≥67.0
|
|
Moisture Content
|
%
|
≤1.5
|
|
Residue in 325 mesh
|
%
|
≤0.02
|
|
PH
|
|
5~7
|
|
Loss after ignition
|
%
|
13.0~14.0
|
|
SiO2
|
％
|
≤47.0
|
|
Al2O3
|
%
|
≥37.0
|
|
Fe2O3
|
%
|
≤0.6
|
*Packing: 25 kg/bag; 50 kg/bag; 1000 kg/bag or according to the customer request
|
|
|
|
|